Lampworking
Glass selection
Lampworking can be done with many types of glass, but the most common are soda-lime glass, sometimes called "soft glass," and borosilicate glass, often called "hard glass.
By sdvs sdvasd
Category: 0
Submit your Articles Here!
Glass selection Lampworking can be done with many types of glass, but the most common are soda-lime glass, sometimes called "soft glass," and borosilicate glass, often called "hard glass." Many artists also use Pyrex. Leaded glass tubing was commonly used in the manufacture of neon signs, although its use has been fading due to environmental concerns and health risks. The colors of the glass must be selected for compatibility with each other, both chemically (more of a concern with soft glass than borosilicate) and in terms of coefficient of thermal expansion (COE) [CTE is also used for Coefficient of Thermal Expansion.] Glass with incompatible COE, mixed together, can create powerful stresses within a finished piece as it cools, cracking or violently shattering the piece. Major types of glass, e.g., borosilicate and soda-lime glass, are not compatible with each other. Chemically, some colors can react with each other when melted together. This may cause desirable effects in coloration, metallic sheen, or result in an aesthetically pleasing "web effect". It also can cause undesirable effects such as unattractive discoloration, bubbling, or devitrification.
Borosilicate glass is considered more forgiving to work with, as its lower COE makes it less apt to crack during flameworking than soda-lime glass. However, it has a narrower working temperature range than soda-lime glass, has fewer available colors, and is considerably more expensive. Also, its working range is at higher temperatures than soda-lime glass, requiring larger torches and the use of oxygen instead of air. In addition to producing a hotter flame, the use of pure oxygen allows more control over the flame's oxidizing or reducing properties, which is necessary because some coloring chemicals in borosilicate glass react with any remaining oxygen in the flame either to produce the desired final color or to discolor if extra oxygen is present.
Tools
Tools for lampworking are similar to those used in glassblowing. Marvers - flat surfaces used to roll glass upon in order to shape, smooth or consolidate applied decoration, typically made of graphite or steel, rods, and other shapes are used to marver or shape the glass. Brass, graphite, or wooden molds (usually of apple or cherry wood) can be used to mold the hot glass. Tungsten picks can be used to drag glass around on the surface, or to bore a hole through a piece. Steel jacks, usually coated with beeswax, are used to neck down or cut off a piece. The importance of graphite in glassblowing is due to its very low density and thus its ability to absorb heat, this allows the graphite to touch the molten glass with minimal temperature contrast between the metal and glass. The graphite absorbs the heat energy so there is minimal shock to the glass, which is the ultimate goal. There is a wide array of glass blowing tools made of graphite for this reason.
General methods of beadmaking
Demonstration of the lampworking process
After designing a piece, a lampworker must plan how to construct it. Once ready to begin, the lampworker slowly introduces glass rod or tubing into the flame to prevent cracking from thermal shock. The glass is heated until molten, wound around a specially-coated steel mandrel, forming the base bead. The coating is an anti-fluxing bead release that will allow the bead to be easily removed from the mandrel. It can then be embellished or decorated using a variety of techniques and materials. All parts of the workpiece must be kept at similar temperatures lest they shatter. Once finished the piece must be annealed in an oven to prevent cracking or shattering.
Annealing, in glass terms, is heating a piece until its temperature reaches a stress-relief point, that is, a temperature at which the glass is still too hard to deform, but is soft enough for internal stresses to ease. The piece is then allowed to heat-soak until its temperature is uniform throughout. The time necessary for this depends on the type of glass and thickness of the thickest section. The piece is then slowly cooled at a predetermined rate until its temperature is below a critical point, at which it can't generate internal stresses, and then can safely be dropped to room temperature. This relieves the internal stresses, resulting in a piece which should last for many years. Glass which has not been annealed may crack or shatter due to a seemingly minor temperature change or other shock.
Types of Glass
Rod vs. sheet
Most lampworkers use rods of glass 78 mm in diameter, though pre-made stringers are available in 13 mm sizes, or rods of 15 mm or more. Sheet glass can be cut with tools into strips, though it is easier to manipulate if attached to a rod first. Glass is also available in particles of various sizes (frit or powder), which is typically used for surface decorations in lampworked beads. Many manufacturers who once only sold their glass in sheet or very thick rod now provide rods for lampworking use. Window glass is usually not used, as it is not formulated for flameworking and there is little variation of color available.
Soda lime glass
This section requires expansion.
The most popular glass for lampworking is soda-lime glass, which is available pre-colored. Soda-lime glass is the traditional mix used in blown furnace glass, and lampworking glass rods were originally hand-drawn from the furnace and allowed to cool for use by lampworkers. Today soda-lime, or "soft" glass is manufactured globally, including Italy, Germany, Czech Republic, China and America.
Lead
In addition to soda lime glass, lampworkers can use lead glass. Lead glasses are distinguished by their lower viscosity, heavier weight, and somewhat greater tolerance for COE mismatches.
Borosilicate
Beadmakers can use borosilicate glass, a very hard glass requiring greater heat. This is laboratory glass, such as Pyrex. At one time, soft (soda lime and lead) and hard (borosilicate) glasses had distinctly different looking palettes, but demand by soft-glass artists for the silver strike colors on the one hand, and the development of the bright, cadmium based `crayon colors' in the boro line on the other, has diminished the distinctions between them.
Basic "Wound Bead" technique
Preparing the mandrel - The beadmaker starts by dipping a mandrel, or wire (stainless steel welding wire, cut into lengths) into a clay based substance (commonly referred to as "bead release") and letting it dry.
Heating rod and mandrel - The flameworker selects rods of glass to heat in the flame of the torch. When both glass and mandrel are sufficiently warm, the beadmaker starts rotating the mandrel while allowing the glass to wind upon it.
Shaping the bead - Beads are shaped using a combination of heat, gravity and tools such as graphite paddles, mashers, tweezers, and picks. Presses to create shapes and indent patterns into the glass are also used.
Decorating the bead - Beads can be decorated by melting stringers, or fibers of glass on the surface, creating dots or lines. With a sharp pointed tool, feathers, hearts or other designs may be produced. Metal decorations of copper, silver, gold, palladium and platinum are applied as metal leaf, wire, mesh or fuming.
Striking - If silver based colors are used (striking colors), the bead must be heated for a few moments in the torch flame or kiln to allow crystals to reform in the glass. This temperature is slightly above the stress relief point.
Annealing - Once completed, beads should be heated to 940-1050F (depending on glass type), until the piece reaches its "stress relief point", held at that temp for a short time, then slowly cooled to avoid thermal shock.
Cold working - The cooled bead can be further decorated. Standard cold working techniques can be employed such as sandblasting, faceting and polishing. Etching the finished piece with acid leaves a matte finish.
Additional techniques for lampworked beads
Beads can be sandblasted, or they can be faceted, using lapidary techniques. "Furnace glass" beads, more elaborate versions of the old seed bead technique described above, are also being made. Chevron beads are multi-layer beads once exclusively made using hot-shop techniques to produce the original tubing; but now some lampworkers make similar designs on their torches before lapping the ends to reveal the various layered colors. As torches get bigger and more powerful, the cross-over between lampworking and furnace glass continues to increase.
Fuming is a technique that has been developed in the past 15 years and consists of heating silver or gold in the flame, so that the metals vaporize or "fume" microscopically thin layers of particles onto the glass. These particle stick to the hot glass surface changing its color with interesting effects. Silver turns clear glass into a yellowish color, giving shades of blues and greens when backed with a dark color, while gold turns clear glass shades of pinks and reds. The precious metal coating becomes increasingly visible the more the glass is fumed.
Brief history of modern lampworked beads
Lampworked beads (with the exception of Asian and African beadmaking) have generally been the provenance of Italian, and, later, Bohemian lampworkers for the last four hundred years or so who kept the techniques secret. Thirty or so years ago, some American artists started experimenting with the form. Their early efforts, by today's standards, were crude, as there was almost no documentation, and none of the modern tools. However, they shared their information, and some of them started small businesses developing tools, torches and other equipment.
This group eventually formed the basis for the International Society of Glass Beadmakers.
See also
Glass beadmaking
Paperweight collecting
v d e
Glass forming techniques
Commercial techniques
Float glass process Blowing and pressing (containers) Extrusion / Drawing (fibers, glasswool) Drawing (optical fibers) Precision glass moulding Overflow downdraw method Pressing Casting Cutting Flame polishing Chemical polishing Diamond turning Rolling
Artistic and historic techniques
Beadmaking Blowing Blown plate Broad sheet Caneworking Crown glass Cylinder blown sheet Engraving Etching Fourcault process Fusing Lampworking Machine drawn cylinder sheet Millefiori Polished plate Slumping Stained glass fusing Stained glass production
See also
Glossary of glass art terms
External links
Lampworking School
The Design Museum: Leopold and Rudolf Blaschka
The International Society of Glass Beadmakers
Corning Museum of Glass
Lampwork bead shapes
ASGS
Categories: Beadwork | Glass art | Glass formingHidden categories: Articles to be expanded from May 2008 | All articles to be expanded
I am an expert from China Quality Dress, usually analyzes all kind of industries situation, such as wholesale cast iron cookware , stainless steel cook ware.
|